Uranium removal from mining water using Cu substituted hydroxyapatite
Résumé
In this study, synthetic copper substituted hydroxyapatite (Cu-Hap), Cu x Ca 10-x (PO 4) 6 (OH) 2 were prepared by co-precipitation method and were used as reactive materials in batch experiments to immobilize uranyl. The limit of incorporation of Cu into a single-phased Cu-Hap reached x Cu ≤1.59. The synthetic Cu-Hap samples obtained with various Cu contents were contacted with synthetic uranyl doped solutions and with real mining waters showing various pH and chemical compositions. A fast and strong decrease of the uranium concentration was observed, followed by the establishment of an equilibrium after 1-4 days of contact with the solutions. Examination of the solid phase after uranium uptake was performed using a combination of techniques. Depending on the composition of the solution and the copper content of the Cu-Hap, various mechanisms of uranium removal were observed. Based on the experimental results and geochemical simulations, it appeared that the main interest for using Cu-Hap is to enlarge the domain of water compositions for which the precipitation of meta-torbernite, (H 3 O) 0.4 Cu 0.8 (UO 2) 2 (PO 4) 2 ·7.6 H 2 O is the predominant mechanism associated to the uranium removal, especially for pH > 6.7 where carbonate uranium species are predominant.
Domaines
Radiochimie
Fichier principal
Metatorbernite-final.pdf (1.79 Mo)
Télécharger le fichier
Supporting information-revised.pdf (1.66 Mo)
Télécharger le fichier
| Origine | Fichiers produits par l'(les) auteur(s) |
|---|
Loading...