Interband cascade Lasers with AlGaAsSb cladding layers emitting at 3.3 µm

Abstract : We investigate the impact of the growth conditions of AlGaAsSb cladding layers on the properties of interband cascade lasers (ICLs). For an optimized structure emitting at 3.3 µm, we achieve an internal quantum efficiency of 65% per stage in good agreement with conventional ICL using InAs/AlSb superlattice cladding layers, in spite of internal losses of 15 cm −1 due to higher optical losses in the n-type AlGaAsSb alloys. Finally, we report a narrow ridge ICL emitting at 3.33 µm operating in continuous wave up to 80°C that produces 1 mW/uncoated facet at 80°C, 10 mW at 40°C and more than 12 mW at 20°C.
Type de document :
Article dans une revue
Liste complète des métadonnées

Littérature citée [36 références]  Voir  Masquer  Télécharger

https://hal.umontpellier.fr/hal-02345145
Contributeur : Laurent Cerutti <>
Soumis le : lundi 4 novembre 2019 - 13:59:54
Dernière modification le : mardi 3 décembre 2019 - 13:06:32

Fichier

oe-27-22-31425.pdf
Fichiers éditeurs autorisés sur une archive ouverte

Identifiants

Citation

D. Díaz-Thomas, Oleksandr Stepanenko, M. Bahriz, Stéphane Calvez, E. Tournié, et al.. Interband cascade Lasers with AlGaAsSb cladding layers emitting at 3.3 µm. Optics Express, Optical Society of America, 2019, 27 (22), pp.31425. ⟨10.1364/OE.27.031425⟩. ⟨hal-02345145⟩

Partager

Métriques

Consultations de la notice

31

Téléchargements de fichiers

29