Mg 3 (BH 4 ) 4 (NH 2 ) 2 as Inorganic Solid Electrolyte with High Mg 2+ Ionic Conductivity

Abstract : Mg 3 (BH 4) 4 (NH 2) 2 compound was synthesized through the investigation of the Mg(BH 4) 2-Mg(NH 2) 2 phase diagram; its crystal structure was solved in a tetragonal unit cell with the space group I4̅. Interestingly, Mg 3 (BH 4) 4 (NH 2) 2 has a high thermal stability with a decomposition temperature above 190°C and exhibits a high Mg 2+ ionic conductivity of 4.1 × 10 −5 S•cm −1 at 100°C with a low activation energy (0.84 eV). The reversible Mg deposition/stripping was demonstrated at 100°C when using Mg 3 (BH 4) 4 (NH 2) 2 as solid electrolyte. Thus, Mg 3 (BH 4) 4 (NH 2) 2 is a compound that could help to develop rechargeable Mg-ion solid-state batteries.
Type de document :
Article dans une revue
Domaine :
Liste complète des métadonnées

https://hal.umontpellier.fr/hal-02924388
Contributeur : Icg Aigle Connectez-vous pour contacter le contributeur
Soumis le : mardi 1 décembre 2020 - 09:08:55
Dernière modification le : mercredi 1 décembre 2021 - 15:00:08
Archivage à long terme le : : mardi 2 mars 2021 - 18:13:58

Fichier

Paper Mg3(BH4)4(NH2)2_ACS Appl...
Fichiers produits par l'(les) auteur(s)

Identifiants

Citation

Ronan Le Ruyet, Benoit Fleutot, Romain Berthelot, Yasmine Benabed, Geoffroy Hautier, et al.. Mg 3 (BH 4 ) 4 (NH 2 ) 2 as Inorganic Solid Electrolyte with High Mg 2+ Ionic Conductivity. ACS Applied Energy Materials, ACS, 2020, 3 (7), pp.6093-6097. ⟨10.1021/acsaem.0c00980⟩. ⟨hal-02924388⟩

Partager

Métriques

Consultations de la notice

145

Téléchargements de fichiers

315