Synthesis of TiO2–ZrO2 Mixed Oxides via the Alginate Route: Application in the Ru Catalytic Hydrogenation of Levulinic Acid to Gamma-Valerolactone - Université de Montpellier Accéder directement au contenu
Article Dans Une Revue Energies Année : 2019

Synthesis of TiO2–ZrO2 Mixed Oxides via the Alginate Route: Application in the Ru Catalytic Hydrogenation of Levulinic Acid to Gamma-Valerolactone

Résumé

In this work, high surface area mono-and binary oxide materials based on zirconia and titania synthetized via the alginate route were applied as supports of ruthenium catalysts used in levulinic acid hydrogenation towards γ-valerolactone. The physicochemical properties of the catalysts were investigated using surface (like time-of-flight secondary ion mass spectrometry (ToF-SIMS), transmission electron microscopy (TEM)) and bulk techniques (temperature-programmed reduction (TPR), X-ray diffraction (XRD)). The obtained results exhibited that the proposed synthesis method allows for modification of the shape, morphology, and surface properties of the studied materials. These catalysts were tested in levulinic acid hydrogenation, in which catalytic support is known to be crucial. The results revealed that the titania-supported catalyst was the most active in the reaction mentioned above, while the highest mechanical stability was observed for zirconia-supported materials.

Domaines

Chimie
Fichier principal
Vignette du fichier
energies-12-04706.pdf (2.63 Mo) Télécharger le fichier
Origine : Fichiers éditeurs autorisés sur une archive ouverte
Loading...

Dates et versions

hal-02456439 , version 1 (06-07-2020)

Licence

Paternité

Identifiants

Citer

Agnieszka Ruppert, Pierre Agulhon, Jacek Grams, Malgorzata Wąchała, Joanna Wojciechowska, et al.. Synthesis of TiO2–ZrO2 Mixed Oxides via the Alginate Route: Application in the Ru Catalytic Hydrogenation of Levulinic Acid to Gamma-Valerolactone. Energies, 2019, 12 (24), pp.4706. ⟨10.3390/en12244706⟩. ⟨hal-02456439⟩
46 Consultations
58 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More