Dielectric Characterization of Core-Shell Structured Poly(vinylidene fluoride)-grafted-BaTiO3 Nanocomposites

Résumé

Dielectric properties of poly(vinylidene fluoride)-grafted-BaTiO3 (PVDF-g-BT) core-shell structured nanocomposites obtained from Reversible Addition Fragmentation chain Transfer (RAFT) polymerization of VDF were investigated by Broadband Dielectric Spectroscopy (BDS). The dielectric constant increased along with the BT content, about +50% by addition of 15 vol% of BT, which was around 40% more than expected from predictions using the usual dielectric modeling methods for composite materials, to be ascribed to the effect of the interfacial core-shell structure. The known dielectric relaxations for PVDF were observed for the neat polymer as well as for its nanocomposites, not affected by the presence of nanoparticles. A relaxation process at higher temperatures was found, due to interfacial polarization at the amorphous-crystalline interface, due to the high crystallinity of materials produced by RAFT. Isochronal BDS spectra were exploited to detect the primary relaxation of the amorphous fraction. Thermal analysis demonstrated a very broad endotherm at temperatures much lower than the usual melting peaks, possibly due to the ungrafted fraction of the polymer that is more easily removable by repeated washing of the pristine material with acetone.
Fichier principal
Vignette du fichier
polymers-15-00595-v4.pdf (2.91 Mo) Télécharger le fichier
Origine Fichiers éditeurs autorisés sur une archive ouverte
Licence

Dates et versions

hal-04039271 , version 1 (01-06-2023)

Licence

Identifiants

Citer

Fatima Ezzahra Bouharras, Massimiliano Labardi, Elpidio Tombari, Simone Capaccioli, Mustapha Raihane, et al.. Dielectric Characterization of Core-Shell Structured Poly(vinylidene fluoride)-grafted-BaTiO3 Nanocomposites. Polymers, 2023, 15 (3), pp.595. ⟨10.3390/polym15030595⟩. ⟨hal-04039271⟩
40 Consultations
14 Téléchargements

Altmetric

Partager

More